| Specifications | ||||
| Material | Coulour | Reference | Packaging | Origin |
| PS | White | rPS67WH | Big bag on pallet | 97% post-consumer plastic |
| Properties | ISO standards | Values | Unit |
| MFI200°/5KG Flexural modulus Notched Izod at 23°C Density |
ISO 1133 ISO 178 ISO 180/1A ISO 1183 |
[5 ; 7] >1700 [6 ; 8] 1.04 |
g/10min MPa kJ/m2 g/cm3 |
| PROCESSING INFORMATION | |
| Pre-drying | Hot air or desiccant |
| Drying temperature | 80°C |
| Drying time | 2-4 hours |
| Injection moulding | |
| Melting point range | 210-230°C |
| Recommended melting point | 215°C |
| Mould temperature range | 50-70°C |
| Recommended mould temperature | 60°C |
Please note that the above information is taken from the average values of different batches. Due to the nature of the raw materials, these values may vary. It is the customer’s responsibility to optimise processing conditions and to ensure suitability with the use of their own products. It is also recommended for the material to be pre-dried prior to use.